Good Solderability Conductive Silver Paste 80% Silver Contain 30 - 65 Viscosity

Good quality Solar Cell Paste for sales
Good quality Solar Cell Paste for sales
The company considerate after-sales service ,And try their best to meet the requirement of customers. We will be a long-term cooperation.

—— Mr. Tehrani

Very appreciate for your professional service & higher standard quality control,very happy to work with LEED!

—— Ronaldo

We trust the quality of your products. It always the best. Keep this going, and we will establish a long-term trade relationship with you.

—— Mr. Mac Cameron

I'm Online Chat Now

Good Solderability Conductive Silver Paste 80% Silver Contain 30 - 65 Viscosity

China Good Solderability Conductive Silver Paste 80% Silver Contain 30 - 65 Viscosity supplier

Large Image :  Good Solderability Conductive Silver Paste 80% Silver Contain 30 - 65 Viscosity

Product Details:

Place of Origin: China
Brand Name: LEED-INK
Certification: ISO9001, ISO14001, SGS, ROHS
Model Number: DT5572

Payment & Shipping Terms:

Minimum Order Quantity: 1KG
Price: Negotiable
Packaging Details: 1KG/ Plastic Jar, 6 Jars/ Carton. Carton Size: 39*26*17cm, G.W.: 7.5KG/ Carton
Delivery Time: Within 7 days after payment confirmed
Payment Terms: L/C, T/T, Western Union, Paypal
Supply Ability: 3000KG per Month
Detailed Product Description
Viscosity: 30-65 Drying: 150-180℃/ 3 Min
Firing: 600-650℃/ 3 Min Fired Thickness(μm): 12-15
Conductivity(mΩ/sq): ≤3 Adhesion((N): ≥130
Ag Content: 78-82%

 

Good Solderability Conductive Silver Paste 80% Silver Contain 30 - 65 Viscosity

 

Description

DT5572 (80% silver contain) is a well-developed conductive silver paste with high performance in printing hot wire for automotive backlights. This product does not contain toxic elements such as lead, in line with the EU ROHS Directive (2002/95/E).
Advantages of our conductive paste product: good printability & solderability, high adhesion & resistance stability.

 

Application

The silver paste is mainly applied on automobile electrically heated glass for defroster and/or defogger purposes.

It forms the pattern on the automobile glass through the silk screen printing process. After drying and heating process, the metal silver conductive wire is formed on the automobile glass. When the power is electrified, the heat can be generated and the frost on the glass can be removed.

The firing range is adapted to suit toughened glass requirements.

 

Specification

 

Test Properties
DT5572
Ag Content (%) 78-82

Viscosity (Pa.S)

(NDJ-99,4#,10rpm,25±0.5℃)

30-65
Fineness(μm) ≤15

Screen Mesh

(Polyester mesh)

200~280
Leveling Time At room temperature, 2-3min

Recommended

Drying Conditions

150-180℃/3min

Recommended

Firing Conditions

600-650℃/3min
Fired Thickness(μm) 12-15
Conductivity(mΩ/sq) ≤3
Drift of Resistance after Reliability Test (%) <10
Adhesion((N) ≥130
Shelf Life Six Months from Date of Shipment

 

Featured Advantage

 

1. Wide firing temperature range
The firing temperature range is wide as 600-650℃ and it could meet most production process requirement.

2. Small change of resistance with long-time printing

The resistance drift could be controlled within 10% during lab testing. It shows the paste could keep stable performance after printing and firing process.

3. Good Acid Resistance

Put the sample soaked in 0.1N sulfuric acid solution(at room temperature) for at least 2 hours, remove the silver layer with adhesive tape and no Ag transfer, and the resistance drift is less than or equal to 8%.

4. Excellent anti-oxidation and anti-sulfide properties

Put the sample soaked in 400g ethanol plus 1g sulfur powder(elemental sulfur) solution for over 2 hours, the surface shall no significant change(yellow or black).

 

Why Choose Us?

1. Dedicated to high quality, stable supply and considerate service.

2. To inform customers of price trends in the market timely.

3. Provide considerate services to minimize clients’ worries.

4. Fast delivery: quick supply of sample in stock and 3-7 days for bulk production.

5. Customiszed production for different paste electrical properties requirements.

 

Contact Details
Hunan LEED Electronic Ink Co., Ltd

Send your inquiry directly to us (0 / 3000)