Adhesive Silver Conductive Paste , Windshield Conductive Thermal Paste

Good quality Solar Cell Paste for sales
Good quality Solar Cell Paste for sales
The company considerate after-sales service ,And try their best to meet the requirement of customers. We will be a long-term cooperation.

—— Mr. Tehrani

Very appreciate for your professional service & higher standard quality control,very happy to work with LEED!

—— Ronaldo

We trust the quality of your products. It always the best. Keep this going, and we will establish a long-term trade relationship with you.

—— Mr. Mac Cameron

I'm Online Chat Now

Adhesive Silver Conductive Paste , Windshield Conductive Thermal Paste

China Adhesive Silver Conductive Paste , Windshield Conductive Thermal Paste supplier

Large Image :  Adhesive Silver Conductive Paste , Windshield Conductive Thermal Paste

Product Details:

Place of Origin: China
Brand Name: LEED-INK
Certification: ISO9001, ISO14001, SGS, ROHS
Model Number: DT557X

Payment & Shipping Terms:

Minimum Order Quantity: 1KG
Price: Negotiable
Packaging Details: 1KG/ Plastic Jar, 6 Jars/ Carton. Carton Size: 39*26*17cm, G.W.: 7.5KG/ Carton
Delivery Time: Within 7 days after payment confirmed
Payment Terms: L/C, T/T, Western Union, Paypal
Supply Ability: 3000KG per Month
Detailed Product Description
Viscosity: 35-85 Pa.s Fineness: ≤20
Drying: 150-180℃/ 3 Min Firing: 600-650℃/ 3 Min
Fired Thickness(μm): 8-15 Conductivity(mΩ/sq): ≤3-12
Adhesion((N): ≥80-130

 

Strong Welding Adhesion Conductive Silver Paste for Automotive Front Windshield

 

Description

LEED-INK Silver paste DT557X series is environmental conductive paste specially designed for automobile front windshield defogging. It is non-toxic up to European RoHS environmental regulation (2002/95/EC). It is with excellent adhesion and good oxidation resistance.

It is heavy-metal free and in compliance with the European legislation for end of life vehicles 2000/53/EC. All our standard compositions are provided with features of viscosity, which make them ready for use in order to get an optimal printing by using standard operating conditions on the part of the client.

 

Application

DT557X series silver paste is mainly applied on automotive electrically heated glass for defroster and/or defogger purposes. It forms the pattern on the automobile glass through the silk screen printing process. After drying and heating process, the metal silver conductive wire is formed on the automobile glass. When the power is electrified, the heat can be generated and the frost on the glass can be removed.

 

Specification

 

Test Properties
DT5571 DT5572 DT5573 DT5574 DT5575
Ag Content (%) 80 75 70 65 60

Viscosity (Pa.S)

(NDJ-99,4#,10rpm,25±0.5℃)

60±25
Fineness(μm) <20

Screen Mesh

(Polyester mesh)

150~250
Leveling Time At room temperature, 2-3min

Recommended

Drying Conditions

150-180℃/3min

Recommended

Firing Conditions

600-650℃/3min
Fired Thickness(μm) 8-15
Conductivity(mΩ/sq) ≤3 ≤4 ≤7 ≤10 ≤12
Drift of Resistance after Reliability Test (%) <10
Adhesion((N) ≥130 ≥130 ≥130 ≥130 ≥80
Shelf Life Six Months from Date of Shipment

 

Featured Advantage

 

1. Strong adhesion, good welding strength

DT557X-H series is with excellent adhesion. The silver paste exhibit a minimum degree of silver migration stain into the glass, after being fired. There ‘s no loss of adhesion or continuity between the conductors and the backlite.

2. Small change of resistance with long-time printing

The resistance drift could be controlled within 10% during lab testing. It shows the paste could keep stable performance after printing and firing process.

3. Good Acid Resistance

Put the sample soaked in 0.1N sulfuric acid solution(at room temperature) for at least 2 hours, remove the silver layer with adhesive tape and no Ag transfer, and the resistance drift is less than or equal to 8%.

4. Excellent anti-oxidation and anti-sulfide properties

Put the sample soaked in 400g ethanol plus 1g sulfur powder(elemental sulfur) solution for over 2 hours, the surface shall no significant change(yellow or black).

5. Good compatibility with black glaze

The product has good compatibility with common black glaze products on the market. After the silver paste firing, the silver line is invisible through the black glaze from the printing reverse side, which shows good compatibility with the black glaze.

 

 