Strong Adhesion Silver Paste Thermal Conductivity , 80% Ag Purity Conductive Paste

Good quality Solar Cell Paste for sales
Good quality Solar Cell Paste for sales
The company considerate after-sales service ,And try their best to meet the requirement of customers. We will be a long-term cooperation.

—— Mr. Tehrani

Very appreciate for your professional service & higher standard quality control,very happy to work with LEED!

—— Ronaldo

We trust the quality of your products. It always the best. Keep this going, and we will establish a long-term trade relationship with you.

—— Mr. Mac Cameron

I'm Online Chat Now

Strong Adhesion Silver Paste Thermal Conductivity , 80% Ag Purity Conductive Paste

China Strong Adhesion Silver Paste Thermal Conductivity , 80% Ag Purity Conductive Paste supplier

Large Image :  Strong Adhesion Silver Paste Thermal Conductivity , 80% Ag Purity Conductive Paste

Product Details:

Place of Origin: China
Brand Name: LEED-INK
Certification: ISO9001, ISO14001, SGS, ROHS
Model Number: DT5571-H

Payment & Shipping Terms:

Minimum Order Quantity: 1KG
Price: Negotiable
Packaging Details: 1KG/ Plastic Jar, 6 Jars/ Carton. Carton Size: 39*26*17cm, G.W.: 7.5KG/ Carton
Delivery Time: Within 7 days after payment confirmed
Payment Terms: L/C, T/T, Western Union, Paypal
Supply Ability: 3000KG per Month
Detailed Product Description
Viscosity: 25-45 Pa.s Fineness: ≤15
Screen Mesh: 150~250 Polyester Mesh Drying: 150-180℃/ 3 Min
Firing: 680-720℃/ 3 Min Conductivity(mΩ/sq): ≤4
Adhesion((N): ≥130

 

Strong Adhesion Silver Paste Thermal Conductivity , 80% Ag Purity Conductive Paste

 

Description

LEED-INK produces a great variety of silver-based pastes for the sector of automotive glasses. Our products are used for the production of interior rear view mirrors, tempered-glass laminated windows and windshields for supplementary alarm, radio aerials and defrost systems. 

Silver paste DT5571-H is with 80% Ag content and with excellent adhesion, good oxidation resistance, and also has good compatibility with common black glaze on the market. It is non-toxic up to European RoHS environmental regulation (2002/95/EC).

 

Applications

DT5571-H series silver paste is mainly applied oncar rear window glass for defroster and/or defogger purposes.

It forms the pattern on the automobile glass through the silk screen printing process. After drying and heating process, the metal silver conductive wire is formed on the automobile glass. When the power is electrified, the heat can be generated and the frost on the glass can be removed.

 

Specifications

 

Test Properties
DT5571-H

Solid Content (%)

85±2

Viscosity (Pa.S)

(Brookfield DV-1,14# spindle,10 rmp,

25℃±0.5℃)

25-45

Fineness(μm)

≤15

Screen Mesh

(Polyester mesh)

150~250

Leveling Time

At room temperature, 2-3min

Recommended

Drying Conditions

150-180℃/3min

Recommended

Firing Conditions

680-720℃/3min

Fired Thickness(μm)

8-12

Conductivity(mΩ/sq)

≤4

Adhesion((N)

≥130

Acid Resistance Qualified. Conditon: The samples were soaked in 0.1N sulfuric acid solution after 2 hours (at room temperature), with tape attached to exposing the silver layer no Ag transfer, resistance drift is less than or equal to 8%.
Anti Vulcanization Qualified. Condition: The sample was soaked in 400g ethanol +1g sulfur powder (elemental sulfur) solution for 2 hours (at room temperature), no obvious change in appearance (yellow or black)

Shelf Life

Six Months from Date of Shipment

 

Feature Advantage

 

1. Strong adhesion, good welding strength

DT557X-H series is with excellent adhesion. The silver paste exhibit a minimum degree of silver migration stain into the glass, after being fired. There ‘s no loss of adhesion or continuity between the conductors and the backlite.

2. Small change of resistance with long-time printing

The resistance drift could be controlled within 10% during lab testing. It shows the paste could keep stable performance after printing and firing process.

3. Good Acid Resistance

Put the sample soaked in 0.1N sulfuric acid solution(at room temperature) for at least 2 hours, remove the silver layer with adhesive tape and no Ag transfer, and the resistance drift is less than or equal to 8%.

4. Excellent anti-oxidation and anti-sulfide properties

Put the sample soaked in 400g ethanol plus 1g sulfur powder(elemental sulfur) solution for over 2 hours, the surface shall no significant change(yellow or black).

5. Good compatibility with black glaze

The product has good compatibility with common black glaze products on the market. After the silver paste firing, the silver line is invisible through the black glaze from the printing reverse side, which shows good compatibility with the black glaze.

 

Strong Adhesion Silver Paste Thermal Conductivity , 80% Ag Purity Conductive Paste

Strong Adhesion Silver Paste Thermal Conductivity , 80% Ag Purity Conductive Paste

 

Contact Details
Hunan LEED Electronic Ink Co., Ltd

Send your inquiry directly to us (0 / 3000)